Cold rolled and heat treated steel sheet, method of production thereof and use of such steel to produce vehicle parts

ABSTRACT

A cold rolled and heat treated steel sheet having a composition containing the following elements, expressed in percent by weight:
         0.15%≤carbon≤0.6%;   4%≤manganese≤20%;   5%≤aluminum≤15%;   0≤silicon≤2%;   aluminium+silicon≥6.5%;
 
and possibly one or more of the following elements:
   0.01%≤niobium≤0.3%;   0.01%≤titanium≤0.2%;   0.01%≤vanadium≤0.6%;   0.01%≤copper≤2.0%;   0.01%≤nickel≤2.0%;   cerium≤0.1%;   boron≤0.01%;   magnesium≤0.05%;   zirconium≤0.05%;   molybdenum≤2.0%;   tantalum≤2.0%;   tungsten≤2.0%;
 
the remainder being composed of iron and unavoidable impurities caused by elaboration, wherein the microstructure of said steel sheet contains in area fraction, 10 to 50% of austenite, the reminder being regular ferrite and ordered ferrite of D03 structure. A manufacturing method and use of the steel sheet for making vehicle parts is also described.

FIELD OF THE INVENTION

The present invention relates to a low density steel having a tensile strength greater than or equal to 600 MPa with uniform elongation of greater than or equal to 9%, suitable for automotive industry and a method for manufacturing thereof.

BACKGROUND

Environmental restrictions are forcing automakers to continuously reduce the CO₂ emissions of their vehicles. To do that, automakers have several options, whereby their principal options are to reduce the weight of the vehicles or to improve the efficiency of their engine systems. Advances are frequently achieved by a combination of the two approaches.

The present invention is directed in part to the first option, namely the reduction of the weight of the motor vehicles. In this very specific field, there is a two-track alternative.

The first track reduces the thicknesses of the steels while increasing their levels of mechanical strength. Unfortunately, this solution has its limits on account of a prohibitive decrease in the rigidity of certain automotive parts and the appearance of acoustical problems that create uncomfortable conditions for the passenger, not to mention the unavoidable loss of ductility associated with the increase in mechanical strength.

The second track reduces the density of the steels by alloying them with other, lighter metals. Among these alloys, the low-density ones called iron-aluminum alloys have attractive mechanical and physical properties while making it possible to significantly reduce the weight. In this case, low density means a density less than or equal to 7.4.

JP 2005/015909 describes a low density TWIP steels with very high manganese contents of over 20% and also containing aluminum up to 15%, resulting in a lighter steel matrix, but the steel disclosed presents a high deformation resistance during rolling together with weldability issues.

SUMMARY OF THE INVENTION

An object of various embodiments of the present invention is to provide cold-rolled steel sheets that simultaneously have:

-   -   a density less than or equal to 7.4,     -   an ultimate tensile strength greater than or equal to 900 MPa         and preferably equal or above 1000 MPa, and     -   an uniform elongation greater than or equal to 9%.

An additional object of various embodiments of the present invention is to provide steel sheets that also have a good suitability for forming, in particular for rolling and a good weldability and good coatability.

Another object of various embodiments of the present invention is to provide a method for the manufacturing of these sheets that is compatible with conventional industrial applications while being robust towards manufacturing parameters shifts.

The present invention provides a cold rolled and heat treated steel sheet having a composition comprising the following elements, expressed in percent by weight:

-   -   0.15%≤carbon≤0.6%,     -   4%≤manganese≤20%,     -   5%≤aluminum≤15%,     -   0≤silicon≤2%,     -   aluminium+silicon≥6.5%,     -   the remainder being composed of iron and unavoidable impurities         caused by elaboration,     -   wherein the microstructure of said steel sheet comprises in area         fraction, 10 to 50% of austenite, the reminder being regular         ferrite and ordered ferrite of D0₃ structure. In some         embodiments, the steel sheet further comprises one or more of         the following elements:     -   0.01%≤niobium≤0.3%,     -   0.01%≤titanium≤0.2%,     -   0.01%≤vanadium≤0.6%,     -   0.01%≤copper≤2.0%,     -   0.01%≤nickel≤2.0%,     -   cerium≤0.1%,     -   boron≤0.01%,     -   magnesium≤0.05%,     -   zirconium≤0.05%,     -   molybdenum≤2.0%,     -   tantalum≤2.0%,     -   tungsten≤2.0%.

In some embodiments, said austenite phase includes intragranular kappa carbides. In some embodiments, the steel sheet comprises up to 2% of intragranular kappa carbides. In some embodiments, aluminium, manganese and carbon amounts are such that 0.3<(Mn/2Al)×exp(C)<2. In some embodiments, the manganese content is between 7 and 15%. In some embodiments, the aluminium content is equal or higher than 7%, and kappa carbides concentration is higher than 1%. In some embodiments, the steel sheet has a density of less than or equal to 7.4, an ultimate tensile strength higher than or equal to 900 MPa and a uniform elongation higher than or equal to 9%.

The present invention further provides a method of production of a cold rolled and heat treated steel sheet comprising the following steps:

providing a cold rolled steel sheet with a composition comprising the following elements, expressed in percent by weight:

-   -   0.15%≤carbon≤0.6%,     -   4%≤manganese≤20%,     -   5%≤aluminum≤15%,     -   0≤silicon≤2%,     -   aluminium+silicon≥6.5%,     -   the remainder being composed of iron and unavoidable impurities         caused by elaboration,     -   heating said cold rolled steel sheet up to a soaking temperature         between 800 and 950° C. during less than 600 seconds, then         cooling the sheet down to a temperature in a range of 600° C. to         room temperature,     -   reheating the steel sheet to a soaking temperature of 150° C. to         600° C. during 10 s to 250 h, then cooling the sheet.

The present invention also provides parts or vehicles comprising a cold rolled steel sheet according to various embodiments of the present invention.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1(a) is a dark field image of D0₃ structure of a sample from trial E.

FIG. 1(b) shows corresponding diffraction pattern, zone axis [100] D0₃. Arrow indicates the reflection used for the dark field image in FIG. 1(a).

DETAILED DESCRIPTION

In order to obtain the desired steel of present invention, the composition is of significant importance; therefore the detailed explanation of the composition is provided in the following description.

Carbon content is between 0.15% and 0.6% and acts as a significant solid solution strengthening element. It also enhances the formation of kappa carbides (Fe,Mn)₃AlC_(x). Carbon is an austenite-stabilizing element and triggers a strong reduction of the martensitic transformation temperature Ms, so that a significant amount of residual austenite is secured, thereby increasing plasticity. Maintaining carbon content in the above range, ensure to provide the steel sheet with the required levels of the strength and ductility. It also allows reducing the manganese content while still obtaining some TRIP effect.

Manganese content must be between 4% and 20%. This element is gammagenous. The purpose of adding manganese is essentially to obtain a structure that contains austenite in addition to ferrite and to stabilize it at room temperature. The ratio of the manganese content to the aluminum content will have a strong influence on the structures obtained after hot rolling. With a manganese content under 4, the austenite will be insufficiently stabilized with the risk of premature transformation into martensite during cooling at the exit from the annealing line. Moreover, addition of manganese increases the D0₃ domain, allowing getting enough precipitation of D0₃ at higher temperatures and/or at lower amounts of aluminium. Above 20%, there is a reduction in the fraction of ferrite which adversely affects the present invention, as it may make it more difficult to reach the required tensile strength. In a preferred embodiment, the addition of manganese will be limited to 17%.

The aluminium content is between 5% and 15%, preferably between 5.5% and 15%. Aluminium is an alphagenous element and therefore tends to promote the formation of ferrite and in particular of ordered ferrite (Fe,Mn,X)₃Al of D0₃ structure (X is any solute additions, e.g. Si, that dissolves in D0₃).The aluminum has a density of 2.7 and has an important influence on the mechanical properties. As the aluminum content increases, the mechanical strength and the elastic limit also increase although the uniform elongation decreases, due to the decrease in the mobility of dislocations. Below 4%, the density reduction due to the presence of aluminum becomes less beneficial. Above 15%, the presence of ordered ferrite increases beyond the expected limit and affects the present invention negatively, as it starts imparting brittleness to the steel sheet. Preferably, the aluminum content will be limited to less than 9% to prevent the formation of additional brittle intermetallic precipitation.

In addition to the above features, in certain embodiments, manganese, aluminium and carbon contents respect the following relationship:

0.3<(Mn/2Al)×exp(C)<2.

Below 0.3, there is a risk that austenite amount is too low, possibly leading to insufficient ductility. Above 2, it may be possible that the austenite volume fraction goes higher than 49%, thereby reducing the potential of the precipitation of D0₃ phase.

Silicon is an element that allows reducing the density of the steel and is also effective in solid solution hardening. It further has a positive effect of stabilizing D0₃ versus B2 phase. Its content is limited to 2.0% because above that level this element has a tendency to form strongly adhesive oxides that generate surface defects. The presence of surface oxides impairs the wettability of the steel and may produce defects during a potential hot-dip galvanizing operation. In a preferred embodiment, the silicon content will preferably be limited to 1.5%.

The inventors have found out that the cumulated amounts of silicon and aluminium had to be at least equal to 6.5% to obtain the results expected in terms of precipitation of D0₃.

Niobium may be added as an optional element in an amount of 0.01 to 0.1% to the steel of present invention to provide grain refinement. The grain refinement allows obtaining a good balance between strength and elongation and is believed to contribute to improved fatigue performance. But, niobium had a tendency to retard the recrystallization during hot rolling and is therefore not always a desirable element. Therefore it is kept as an optional element.

Titanium may be added as an optional element in an amount of 0.01% to 0.1% to the steel of present invention for grain refinement, in a similar manner as niobium. It further has a positive effect of stabilizing D0₃ versus B2 phase. Therefore, the unbounded part of titanium that is not precipitated as nitride, carbide or carbonitride will stabilize the D0₃ phase.

Vanadium may be added as an optional element in an amount of 0.01% to 0.6%. When added, vanadium can form fine carbo-nitrides compounds during the annealing, these carbo-nitrides providing additional hardening. It further has a positive effect of stabilizing D03 versus B2 phase. Therefore, the unbounded part of vanadium that is not precipitated as nitride, carbide or carbonitride will stabilize the D0₃ phase.

Copper may be added as an optional element in an amount of 0.01% to 2.0% to increase the strength of the steel and to improve its corrosion resistance. A minimum of 0.01% is required to get such effects. However, when its content is above 2.0%, it can degrade the surface aspect.

Nickel may be added as an optional element in an amount of 0.01 to 3.0% to increase the strength of the steel and to improve its toughness. A minimum of 0.01% is required to get such effects. However, when its content is above 3.0%, it tends to stabilize B2 which would be detrimental to D0₃ formation.

Other elements such as cerium, boron, magnesium or zirconium can be added individually or in combination in the following proportions: cerium≤0.1%, B<0.01, Mg≤0.05 and Zr≤0.05. Up to the maximum content levels indicated, these elements make it possible to refine the ferrite grain during solidification.

Finally, molybdenum, tantalum and tungsten may be added to stabilize the D0₃ phase further. They can be added individually or in combination up to maximum content levels: Mo≤2.0, Ta≤2.0, W≤2.0. Beyond these levels the ductility is compromised.

The microstructure of the sheet claimed by the invention comprises, in area fraction, 10 to 50% of austenite, said austenite phase optionally including intragranular (Fe,Mn)₃AlC_(x) kappa carbides, the reminder being ferrite, which includes regular ferrite and ordered ferrite of D0₃ structure and optionally up to 2% of intragranular kappa carbides.

Below 10% of austenite, the uniform elongation of at least 9% cannot be obtained.

Regular ferrite is present in the steel of present invention to impart the steel with high formability and elongation and also, to a certain degree, some resistance to fatigue failure.

D0₃ ordered ferrite in the frame of the present invention, is defined by intermetallic compounds whose stoichiometry is (Fe,Mn,X)₃AI. The ordered ferrite is present in the steel of present invention with a minimum amount of 0.1% in area fraction, preferably of 0.5%, more preferably of 1.0% and advantageously of more than 3%. Preferably, at least 80% of such ordered ferrite has an average size below 30 nm, preferably below 20 nm, more preferably below 15 nm, advantageously below 10 nm or even below 5 nm. This ordered ferrite is formed during the second annealing step providing strength to the alloy by which the levels of 900 MPa can be reached. If ordered ferrite is not present, the strength level of 900 MPa cannot be reached.

Kappa carbide, in the frame of the present invention, is defined by precipitates whose stoichiometry is (Fe,Mn)₃AIC_(x), where x is strictly lower than 1. The area fraction of kappa carbides inside ferrite grains can go up to 2%. Above 2%, the ductility decreases and uniform elongation above 9% is not achieved. In addition, uncontrolled precipitation of Kappa carbide around the ferrite grain boundaries may occur, increasing, as a consequence, the efforts during hot and/or cold rolling. The kappa carbide can also be present inside the austenite phase, preferably as nano-sized particles with a size below 30 nm.

The steel sheets according to the invention can be obtained by any suitable process. It is however preferable to use the method according to the invention that will be described.

In an embodiment, a process according to the invention includes providing a semi-finished casting of steel with a chemical composition within the range of the invention as described above. The casting can be done either into ingots or continuously in form of slabs or thin strips.

For the purpose of simplification, the process according to an embodiment of the invention will be further described taking the example of slab as a semi-finished product. The slab can be directly rolled after the continuous casting or may be first cooled to room temperature and then reheated.

The temperature of the slab which is subjected to hot rolling must be below 1280° C., because above this temperature, there would be a risk of formation of rough ferrite grains resulting in coarse ferrite grain which decreases the capacity of these grains to re-crystallize during hot rolling. The larger the initial ferrite grain size, the less easily it re-crystallizes, which means that reheat temperatures above 1280° C. must be avoided because they are industrially expensive and unfavorable in terms of the recrystallization of the ferrite. Coarse ferrite also has a tendency to amplify the phenomenon called “roping”.

It is desired to perform the rolling with at least one rolling pass in the presence of ferrite. The purpose is to enhance partition of elements that stabilize austenite into austenite, to prevent carbon saturation in the ferrite, which can lead to brittleness. The final rolling pass is performed at a temperature greater than 800° C., because below this temperature the steel sheet exhibits a significant drop in rollability.

In an embodiment of the present invention, the temperature of the slab is sufficiently high so that hot rolling can be completed in the inter-critical temperature range and final rolling temperature remains above 850° C. A final rolling temperature between 850° C. and 980° C. is preferred to have a structure that is favorable to recrystallization and rolling. It is preferred to start rolling at a temperature of the slab above 900° C. to avoid excessive load that may be imposed on a rolling mill.

The sheet obtained in this manner is then cooled at a cooling rate, preferably less than or equal to 100° C./s down to the coiling temperature. Preferably, the cooling rate will be less than or equal to 60° C./s.

The hot rolled steel sheet is then coiled at a coiling temperature below 600° C., because above that temperature there is a risk that it may not be possible to control the kappa carbide precipitation inside ferrite up to a maximum of 2%. A coiling temperature above 600° C. will also result in significant decomposition of the austenite making it difficult to secure the required amount of such phase. Therefore the preferable coiling temperature for the hot rolled steel sheet of the present invention is between 400° C. and 550° C.

An optional hot band annealing can be performed at temperatures between 400° C. and 1000° C. It can be a continuous annealing or a batch annealing. The duration of the soaking will depend on whether it is continuous annealing (between 50 s and 1000 s) or batch annealing (between 6 h and 24 h).

The hot rolled sheets are then cold rolled with a thickness reduction between 35 to 90%.

The obtained cold rolled steel sheet is then subjected to a two-step annealing treatment to impart the steel with targeted mechanical properties and microstructure.

In the first annealing step, the cold rolled steel sheet is heated at a heating rate which is preferably greater than 1° C./s to a holding temperature between 800° C. and 950° C. for a duration less than 600 seconds to ensure a re-crystallization rate greater than 90% of the strongly work hardened initial structure. The sheet is then cooled to the room temperature whereby preference is given to a cooling rate greater than 30° C./s in order to control kappa carbides inside ferrite.

The cold rolled steel sheet obtained after first annealing step can, for example, then again reheated at a heating rate of at least 10° C./h to a holding temperature between 150° C. and 600° C. for a duration between 300 seconds and 250 hours and then cooled down to room temperature. This is done to effectively control the formation of D03 ordered ferrite and, possibly, of kappa carbides inside austenite. Duration of holding depends upon on the temperature used.

An additional heat treatment to facilitate hot dip coating with zinc may be optionally performed. In this additional heat treatment, the steel sheet is reheated to a temperature of 460 to 500° C. Such treatment does not alter any of the mechanical properties or microstructure of the steel sheet.

EXAMPLES

The following tests, examples, figurative exemplification and tables which are presented herein are non-restricting in nature and must be considered for purposes of illustration only, and will display the advantageous features of the present invention.

Samples of the steel sheets according to the invention and to some comparative grades were prepared with the compositions gathered in table 1 and the processing parameters gathered in table 2. The corresponding microstructures of those steel sheets were gathered in table 3.

TABLE 1 Compositions (Mn/ Grade C Mn Al Si Cu S p 2Al) * exp(C) 1 0.19 8.4 6.1 0.91 — 0.005 0.017 0.83 2 0.19 8.4 6.2 0.94 1.10 0.005 0.017 0.82 3 0.22 8.2 7.8 0.27 — <0.001 0.030 0.65 4 0.29 6.5 5.9 0.90 — 0.005 0.020 0.74 5 0.30 6.6 5.8 1.2 — 0.004 0.015 0.77

TABLE 2 Process parameters Hot and cold rolling parameters Reheating FR T Cooling rate Coiling CR Trial Grade T (° C.) (° C.) (° C./s) T (° C.) (%) A 1 1150 920 60 450 75 B* 1 1150 920 60 450 75 C* 1 1150 920 60 450 75 D 2 1150 920 60 450 75 E* 2 1150 920 60 450 75 F* 2 1150 920 60 450 75 G 3 1180 905 50 500 75 H* 3 1180 905 50 500 75 I* 3 1180 905 50 500 75 J 4 1200 950 60 450 75 K* 4 1200 950 60 450 75 L 5 1150 940 100 450 75 M* 5 1150 940 100 450 75 N 5 1150 940 100 450 75 O* 5 1150 940 100 450 75 Annealing parameters First annealing step Second Cooling rate annealing step Trial Grade T (° C.) t (s) (° C./s) T (° C.) t (h) A 1 850 136 100 — — B* 1 850 136 100 400 72 C* 1 850 136 100 400 110  D 2 850 136 100 — — E* 2 850 136 100 400 72 F* 2 850 136 100 400 110  G 3 850 136 100 — — H* 3 850 136 100 400 48 I* 3 850 136 100 400 72 J 4 900 136 100 — — K* 4 900 136 100 400 110  L 5 850 136 65 — — M* 5 850 136 65 400 72 N 5 900 136 65 — — O* 5 900 136 65 400 72 *according to the invention

TABLE 3 Microstructures Regular Austenite ferrite + including D0₃ Kappa in Kappa Kappa in ferrite ferrite D0₃ Trial Grade (%) austenite (%) (%) ferrite A 1 25 Yes ** 75 — No B* 1 25 Yes ** 75 — Yes C* 1 25 — 75 — Yes D 2 25 Yes ** 75 — No E* 2 25 Yes ** 75 — Yes F* 2 25 — 75 — Yes G 3 18 Yes   80 2 No H* 3 18 Yes   80 2 Yes I* 3 18 — 80 2 Yes J 4 31 Yes ** 69 — No K* 4 32 — 68 — Yes L 5 34 Yes ** 66 — No M* 5 34 — 66 — Yes N 5 35 Yes ** 65 — No O* 5 35 — 65 — Yes ** Early stages of Kappa precipitation in austenite detected by transmission electron microscopy

Some microstructure analyses were performed on samples from trial E and images of D0₃ structure are reproduced on FIGS. 1 (a) and 1 (b):

-   -   (a) Dark field image of D0₃ structure     -   (b) Corresponding diffraction pattern, zone axis [100] D0₃.         Arrow indicates the reflection used for the dark field image in         (a)

The properties of those steel sheets were then evaluated, the results being gathered in table 4.

TABLE 4 Properties Trial Grade YS (MPa) UTS (MPa) UE (%) TE (%) Density A 1 623 788 17.6 28.5 7.16 B* 1 870 1008  9.6 16.6 7.16 C* 1 900 1034  9.3 16.2 7.16 D 2 626 788 16.3 25.8 7.15 E* 2 899 1041  9.3 15.1 7.15 F* 2 916 1068  9.1 13 7.15 G 3 633 774 15.5 24.4 7.02 H* 3 771 902 10 18.9 7.02 I* 3 787 913 9.4 19 7.02 J 4 633 795 18.1 29.4 7.18 K* 4 849 976 10.8 18.2 7.18 L 5 692 851 17.9 28.5 7.18 M* 5 878 1024  11 18.8 7.21 N 5 655 840 19.5 31.3 7.21 O* 5 861 1014  11.8 20.7 7.21

The examples show that the steel sheets according to the invention are the only one to show all the targeted properties thanks to their specific composition and microstructures. 

1-9. (canceled)
 10. A cold rolled and heat treated steel sheet having a composition comprising the following elements, expressed in percent by weight: 0.15%≤carbon≤0.6%, 4%≤manganese≤20%, 5%≤aluminum≤15%, 0<silicon≤2%, aluminium+silicon≥6.5%, the remainder being composed of iron and unavoidable impurities caused by elaboration, wherein the microstructure of said steel sheet comprises in area fraction, 10 to 50% of austenite, the reminder being regular ferrite and ordered ferrite of D0₃ structure.
 11. A cold rolled and heat treated steel sheet according to claim 10, wherein aluminium, manganese and carbon amounts are such that 0.3<(Mn/2Al)×exp(C)<2.
 12. A cold rolled and heat treated steel sheet according to claim 10, wherein the manganese content is between 7 and 15%.
 13. A cold rolled and heat treated steel sheet according to claim 10, wherein the aluminium content is equal or higher than 7%, and wherein kappa carbides concentration is higher than 1%.
 14. A cold rolled and heat treated steel sheet according to claim 10, wherein said steel sheet has a density of less than or equal to 7.4, an ultimate tensile strength higher than or equal to 900 MPa and a uniform elongation higher than or equal to 9%.
 15. A method of production of a cold rolled and heat treated steel sheet comprising the following steps: providing a cold rolled steel sheet with a composition according to claim 10, heating said cold rolled steel sheet up to a soaking temperature between 800 and 950° C. during less than 600 seconds, then cooling the sheet down to a temperature in a range of 600° C. to room temperature, reheating the steel sheet to a soaking temperature of 150° C. to 600° C. during 10 s to 250 h, then cooling the sheet.
 16. A cold rolled and heat treated steel sheet according to claim 10, wherein the cold rolled and heat treated steel sheet produced according to the method of claim 15 and is for a manufacture of structural or safety parts of a vehicle.
 17. A structural or safety part of a vehicle comprising a cold rolled and heat treated steel sheet according to claim 10, wherein the structural or safety part is manufactured by a method comprising flexible rolling of said cold rolled and heat treated steel sheet.
 18. A vehicle comprising a structural or safety part according to claim
 17. 19. The cold rolled and heat treated steel sheet of claim 10, further comprising one or more of the following elements: 0.01%≤niobium≤0.3%, 0.01%≤titanium≤0.2%, 0.01%≤vanadium≤0.6%, 0.01%≤copper≤2.0%, 0.01%≤nickel≤2.0%, cerium≤0.1%, boron≤0.01%, magnesium≤0.05%, zirconium≤0.05%, molybdenum≤2.0%, tantalum≤2.0%, tungsten≤2.0%.
 20. The cold rolled and heat treated steel sheet of claim 10, wherein said austenite phase includes intragranular kappa carbides.
 21. The cold rolled and heat treated steel sheet of claim 10, which comprises up to 2% of intragranular kappa carbides. 